US Patent:

20160289452, Oct 6, 2016

Filed:

Jun 15, 2016

Appl. No.:

15/183440

Inventors:

- Tulsa OK, US
Ronnie J. Price - Sapulpa OK, US
Andrew C. Fox - Tulsa OK, US
Richard K. Steger - Broken Arrow OK, US

International Classification:

C08L 95/00
E01C 19/17
E01C 3/00
E01C 3/06
B05D 1/02
E01C 11/00

Abstract:

A sprayable coating composition, and method of application, for coating asphalt paving surfaces. In the coating composition, a low bulk density aggregate material of sprayable particle size is suspended in a sprayable asphalt emulsion in an amount sufficient to increase the micro-texture surface roughness of the cured coating.

US Patent:

20140373750, Dec 25, 2014

Filed:

Jun 9, 2014

Appl. No.:

14/299493

Inventors:

- Tulsa OK, US
Ronnie J. PRICE - Sapulpa OK, US
Andrew C. FOX - Tulsa OK, US
Richard K. STEGER - Broken Arrow OK, US

International Classification:

C09D 195/00
E01C 3/00
E01C 3/06
E01C 11/00

US Classification:

106277, 427138

Abstract:

A sprayable coating composition, and method of application, for coating asphalt paving surfaces. In the coating composition, a low bulk density aggregate material of sprayable particle size is suspended in a sprayable asphalt emulsion in an amount sufficient to increase the micro-texture surface roughness of the cured coating.

US Patent:

20140356526, Dec 4, 2014

Filed:

May 23, 2014

Appl. No.:

14/285750

Inventors:

- Tulsa OK, US
Ronnie J. PRICE - Sapulpa OK, US
Andrew C. FOX - Tulsa OK, US
Joseph LORENC - Philadelphia PA, US
Andrew T. BICKFORD - Goose Creek SC, US

International Classification:

C09D 195/00
B05D 1/02

US Classification:

427136, 524 60

Abstract:

A method of producing a cationic asphalt slurry composition which can be used as an asphalt paving sealer or as a paving or repair composition. In the method and composition, latex and other polymers are used to build viscosity and a pH buffering filler is added to prevent flocculation. Consequently, the cationic composition can be stored without irreversibly settling or separating, and without breaking for several days prior to use. In addition, non-expansive clay and a polar polymer hardening agent are used so that, when applied, the composition will set and develop strength very quickly.